DIN 1.2714 | JIS SKT4 | AISI L6 | UNI T61206 | ASTM L6 | Brand Name Sitherm 2714 | Ravne UTOPEX2 | Mat No 1.2714 | DIN 56NiCrMoV7+ | EN 55NiCrMoV7 | ГОСТ 5ХН2МФ | Hot Work Tool Steel | GB 5CrNiMo | AFNOR 55NCDV7 | BS BH224-5 | UNI 44NiCrMoV7-KU | UNI 56NiCrMoV7-KU | PN WNL | PN WNLV | CSN 19662 | CSN 19663 | ONORM W501 | ONORM W502 | GOST 5KHNM | GOST 5KHNV | ISO 55NiCrMoV7 | WNr 55NiCrMoV6 | WNr 56NiCrMoV7 | Manufacturers & Suppliers in India
DIN 1.2714 Steel Round Bar, DIN 1.2714 Steel Round Bar Manufacturers, DIN 1.2714 Steel Suppliers, DIN 1.2714 Stockist, DIN 1.2714 Steel Dealers, DIN 1.2714 Steel Distributors, DIN 1.2714 Wholesalers, DIN 1.2714 Steel Traders, DIN 1.2714 Steel Square Distributors, DIN 1.2714 Steel Flat Bar, DIN 1.2714 Steel Companies Near me.
PARMANU DHATU NIGAM
THE PARMANU DHATU NIGAM INDIA’S LARGEST INDEPENDENT MULTI-METALS & ALLOYS STOCKHOLDER
PARMANU DHATU NIGAM - INDIA
M: +91-9820061193 | +91-9869542898 | +91-9820325078
Tel: +91-022-67437418
E-Mail: Parmanudhanig@gmail.com
Website: www.parmanudhatu.com | www.parmanudhatunigam.com
Country of Origin: Made in India
Manufacturer: Parmanu Dhatu Nigam
Manufacturer Brand: PARMANU
Grade Introduction:
1.2714 is a German Hot work alloy steel material grade.it is shock-resisting steel. it belongs to DIN 17350 standard. Digital Grade material number W-Nr 1.2714, Metal Steel grade 56NiCrMoV7. It is a die steel, use in extrusion molds, Hot Cast molds. like aluminum production, Aluminum cast mold. Our Tool Steel material 100 % ultrasonic tested at a good price. Small size steel products make by hot rolled, large size steel products make by forging.
Grade Application:
1.2714 cold working tool steel is for general-purpose tools and dies where greater toughness is required, but with some sacrifice of abrasion resistance.
Typically used below applications:
spindles,
forming rolls,
punches,
blanking and forming dies,
trimmer dies,
clutch parts,
pawls,
bearings,
chucks parts,
rollers,
knuckle pins,
clutch pins,
shear blades
Equivalent grades:
USA |
Germany |
China |
Japan |
France |
England |
Italy |
Poland |
Czechia |
Austria |
Russia |
Inter |
– |
DIN,WNr |
GB |
JIS |
AFNOR |
BS |
UNI |
PN |
CSN |
ONORM |
GOST |
ISO |
L6 |
55NiCrMoV6 |
5CrNiMo |
SKT4 |
55NCDV7 |
BH224-5 |
44NiCrMoV7-KU |
WNL |
19662 |
W501 |
5KHNM |
55NiCrMoV7 |
56NiCrMoV7 |
56NiCrMoV7-KU |
WNLV |
19663 |
W502 |
5KHNV |
People also search as:
DIN 1.2714, DIN 1.2714 Steel, DIN 1.2714 Chemical composition, DIN 1.2714 Mechanical properties, DIN 1.2714 Equivalent Grades, DIN 1.2714 Steel plate, DIN 1.2714 Steel sheet, DIN 1.2714 Manufacturers, DIN 1.2714 Suppliers, DIN 1.2714 Dealers, DIN 1.2714 Stockist, DIN 1.2714 Distributors, DIN 1.2714 Wholesalers, DIN 1.2714 Traders.
Chemical composition:
The following table shows the chemical composition of DIN 1.2714 steel:
Element |
C |
Si |
Mn |
Ni |
P |
S |
Cr |
Mo |
V |
Content (%) |
0.5 – 0.6 |
0.1 – 0.4 |
0.6 – 0.9 |
1.5 – 1.8 |
0.03 Max |
0.03 Max |
0.8 – 1.2 |
0.35 – 0.55 |
0.05 – 0.15 |
Mechanical Properties:
Hardness(HB) |
Rp 0.2 Yield Strength |
Rm Tensile Strength |
Elongation |
K C V 20°C |
Elastic modulus | |||
---|---|---|---|---|---|---|---|---|
MPa |
ksi |
MPa |
ksi |
% |
J |
GPa |
ksi | |
376 |
1045 |
151 |
1270 |
184 |
10 |
40 |
205 |
29733 |
Hardness:
Annealing 255 HB max, Q+T: 58-38HRc, different hardness according to different Tempering temperature.
Heat treatment:
Heat treatment temperatures, rate of heating, cooling, and soaking times will vary due to factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium, and workpiece transfer facilities.
Hardening:
Hardening temperature/℃: 840~870, Quenching in oil
Tempering:
Commonly used drawing temperature/℃: 400~650; tempering after-hardening values /MPa|400℃: 1770; tempering after-hardening values /MPa|500℃: 1570; tempering after-hardening values /MPa|600℃: 1320; tempering after-hardening values /MPa|650℃: 1180
Physical Properties:
Density: 7.85kg/m3
Thermal conductivity
Forging ratio: 4:1 Minimum
Microstructure
Magnetic
Thermal Properties:
Thermal conductivity (°C)
|
20
|
350
|
700
|
W/(m*K)
|
35.0
|
39.0
|
36.0
|
Forging Properties:
For forging 1.2714 steel, Slowly Pre-heat, at Hot-working temperature/℃: 1050~850
Stress Relieving:
When tools made from 1.2714 steel are heavily machined or ground, the relief of internal strains is advisable before hardening to minimize the possibility of distortion. Stress-relieving of this grade should be done after rough machining. To stress relief, heat the component carefully to 600-650°C, allow a good soaking period, about two hours per 25mm of section. Cool in the furnace to 500°C then freely in the air. Tools may then be finish machined before hardening.
Normalizing:
Because of its air-hardening ability, 1.2714 – Hot-Work Mould Steel should not be normalized.
Annealing:
Annealing temperature/℃: 680~710; After the annealing, degree of hardness ≤HBS: 250
Density:
Density: 7.85kg/m3
Machinability:
The machinability of tool steel L6 is very good. It rates 90% of the machinability of the W-group water hardening low alloy steels rated 100% as a baseline.
Welding:
Stress tempering for prehardened condition.
1.2714 tool steel,also refers to 56NiCrMoV7 as per German standard DIN 17350.It is improved on the basis of 1.2344 steel, which not only retains the advantages of 1.2344 high plasticity, high toughness and wear resistance, but also has better heat crack resistance.
1.2714 steel not only has good toughness, ductility and crack resistance, but also has high hardenability. The martensite structure can be obtained by air cooling during quenching.After quenching and tempering, 1.2714 steel has small deformation and excellent comprehensive performance.It is suitable for large-scale, complex, precise and long-life die-casting molds, high-performance die-casting molds, extrusion molds, etc.
CHEMICAL COMPOSITION AS PER DIN 17350
Grade | C | Si | Mn | P | S | Cr | Ni | Mo | V |
1.2714/56NiCrMoV7 | 0.50-0.60 | 0.1-0.4 | 0.65-0.95 | ≤0.03 | ≤0.03 | 1.0-1.2 | 1.50-1.8 | 0.45-0.55 | 0.07-0.12 |
1.2714/56NiCrMoV7 EQUIVALENT NATIONAL GRADE
As a member of hot work die steel, 1.2714 steel is highly affirmed by technical engineers all over the world for its excellent hot workability, and has developed similar grades that meet the needs of their respective countries.
Standard | Grade | C | Si | Mn | P | S | Cr | Ni | Mo | V |
ASTM A681 | AISI L6 | 0.65-0.75 | 0.1-0.5 | 0.25-0.80 | ≤0.03 | ≤0.03 | 0.6-1.2 | 1.25-2.0 | ≤0.50 | — |
EN ISO 4957 | 55NiCrMoV7 | 0.50-0.60 | 0.1-0.4 | 0.60-0.90 | ≤0.03 | ≤0.02 | 0.8-1.2 | 1.50-1.8 | 0.35-0.55 | 0.05-0.15 |
JIS G4404 | SKT4 | 0.50-0.60 | 0.1-0.4 | 0.60-0.90 | ≤0.03 | ≤0.02 | 0.8-1.2 | 1.50-1.8 | 0.35-0.55 | 0.05-0.15 |
1.2714/56NiCrMoV7 FORGING PROCESS
Ingot Quality Control
When we forge 1.2714 steel, the first consideration is the quality of the forged steel ingot, which requires us to choose a suitable steelmaking process to control the quality of the billet.
The ingot process for 1.2714/56NiCrMoV7 as below:
Electric Arc Furnace(EAF)→Secondary Refining(LF)→ Vacuum Decarburization(VD)→Ingot Casting
Forging Temperature Control
- Initial Forging Temperature:1100-1150oC
- Heating temperature control:Heating up and holding temperature in stages to ensure that 1.2714 steel is heated evenly.
- Final Forging Temperature:≥850oC
Forging Deformation
When we consider the amount of forging deformation, the first thing that comes to mind is the forging ratio.Through the forging process, an appropriate forging ratio can promote the bubbles, porosity, and micro-cracks in the steel ingot to be welded under the action of compressive stress, and the material density is improved.
For 1.2714 steel,we usually control the forging ratio with Upsetting and Drawing Process,and guarantee it above 4:1
DIN1.2714 Steel Hot Foring with 1600T Forging Press
Post-Forging Treatment
The conventional treatment method is to bury the forged 1.2714 steel in the sand pit for heat preservation, the purpose is to let the material cool down slowly to prevent cracks.
But for 1.2714 steel that is sensitive to white spots, in order to prevent white spots from being produced during the cooling process, dehydrogenation heat treatment should be done in time to allow the hydrogen inside the material to fully diffuse and escape.
1.2714/56NiCrMoV7-THE COMPREHENSIVE FAQ GUIDE
DIN 1.2714/56NiCrMoV7,as Chromium-nickel-molybdenum-vanadium alloy hot work die steel, is known for stable performance.As a special steel grade in hot work die steel, we certainly want to learn more about this particular kind of steel to properly figure more out about it.
Reading our guide,we will guide you to a better and deeper understanding of what 1.2714 steel is, so as to help you choose 2714 steel from a more comprehensive perspective.
WHAT IS HOT WORK TOOL STEEL?
Hot work tool steel refers to alloy tool steel suitable for making molds for thermal deformation processing of metals, such as hot forging dies, hot extrusion dies, die-casting dies, and hot upsetting dies.
Since hot working molds work under high temperature and high pressure conditions for a long time。Therefore, mold materials are required to have high strength, hardness and thermal stability,especially should have high thermal strength, thermal fatigue, toughness and wear resistance.
Hot Work Tool Steel Application
The hot work mold bears a great impact when it is working. The mold cavity is in contact with high-temperature metal and repeated heating and cooling cycles. It can be said that its use conditions are extremely harsh. In order to meet the requirements of the hot work die, the hot work tool steel should have the following basic characteristics:
- High high temperature strength and good toughness
- Good wear resistance
- High thermal stability
- Excellent thermal fatigue resistance
- High hardenability
- Good thermal conductivity
- Good forming process performance
General Hot Work Tool Steel Classification
- Low alloy hot work tool steel:55NiCrMoV6/1.2713,56NiCrMoV7/1.2714
- Medium alloy hot work tool steel:AISI H13 Ι 1.2344,AISI H11/1.2343
- Tungsten hot work tool steel:AISI H21,AISI H22.
QUICK QUESTIONS FOR 1.2714 STEEL
What Is The Hardness For 1.2714 Steel?
Normally, 1.2714 hot work tool steel is used in heat treatment condition.High hardness will be obtained after quenching and tempering.
1.2714 steel will generally be pre-hardened to hardness range of 38-53HRC
The application of specific hardness is roughly as follows:
- Normal use condition,Hardness 46~50HRC
- Small-part extrusion die with heat-resistance cracking as the main performance,Hardness 50~53HRC
- Toughness as the main performance,Hardness 43~46HRC
What Is The Tensile Strength of 1.2714 Steel?
After quenching and tempering heat treatment, 1.2714 steel not only obtained high hardness, correspondingly also obtained high strength.
With hardness 380-420HB,The corresponding tensile strength is from 1200 to 1400Mpa.
Can 1.2714 Steel Be Water Quenched?
1.2714 steel can be water quenched, but as alloy tool steel, The rapid cooling rate of water quenching leads to an increase in the internal stress of the material, and an increase in the tendency of deformation and cracking.
As 1.2714 steel with high hardenability, it is more suitable for oil with a slow cooling rate as a quenching medium.
How Is The Hardenability of 1.2714 Steel?
The hardenability of steel mainly depends on its chemical composition, especially containing alloying elements that increase hardenability. The steel with good hardenability can make the whole section of the steel part obtain uniform mechanical properties.
1.2714 steel has such good hardenability.The Cr. Ni. Mo element is added to 1.2714 steel, mainly to improve the hardenability of the steel, especially when working together, the hardenability is significantly improved.
For example, a mold of 300mm x 300mm x 400mm can be thoroughly hardened, and the hardness of the entire section is uniform.
Can 1.2714 steel Be Machined Easily?
It depends on the heat treatment condition when machining 1.2714 steel.With annealed condition,hardness will below 248HB,it is relatively easy to process.
While after quenched and tempered conditin,harness will exceed 380HB,it is difficult to do turning processing on 1.2714 steel.Fortunately, superhard tool materials, such as CBN tools and PCD tools, can be used to solve this situation.
How To Check Internal Defects of 1.2714 Steel?
The most cost-effective way is ultrasonic testing, which has proven its value.White spots and cracks, the most dangerous defects in the 2714 material, can be directly judged by ultrasonic testing. The pores, looseness and non-metallic inclusions in the material can also be tested by ultrasonic to determine whether they exceed the standard.
Ultrasonic Testing Principle Diagram
HEAT TREATMENT FOR 1.2714 STEEL
How To Annealing 1.2714 Steel?
Although the annealing time is long and the production efficiency is low, 1.2714 steel needs to be annealed under certain circumstances.
- Stress Relief Annealing
Improve or eliminate various structural defects and residual stress caused by 1.2714 steel during forging,rolling and straightening, and prevent material deformation and cracking.
Generally, the stress relief annealing temperature is controlled at 450-500°C,the temperature of stress relief annealing should generally be 20~30℃ lower than the last tempering temperature, so as not to reduce the hardness and mechanical properties.
- Complete Annealing
Also refers to Recrystallization Annealing.Refine the internal grains of 1.2714 steel, uniform structure to improve its mechanical properties, reduce its surface hardness for machining, and prepare the structure for final heat treatment (quenching & tempering).
The complete annealing temperature of 1.2714 steel is controlled at 760-780°C, and the heating rate usually does not exceed 100°C/hour.The holding time should be determined according to the workpiece shape, size,original structure state, furnace capacity, heating equipment and other factors. Generally, it can be calculated according to the thickness of the workpiece for one hour per 20 mm.
The cooling after annealing should be sufficiently slow, and furnace cooling can be used, and the annealing hardness for 1.2714 steel is below 229HB.
How To Quenching And Tempering 1.2714 Steel?
As a member of hot work tool steel, 1.2714 steel is often used in high temperature and harsh working environment, so its performance requirements are high. This requires us to quench and temper it to meet various performance requirements.
- 1.2714 Steel Quenching
From the consideration of quenching medium, our priority is oil.The cooling effect is slower than that of water, which can prevent quenching cracking and serious deformation.
The quenching temperature of 1.2714 steel should be selected within the temperature range where the austenite grains do not grow, generally controlled between 840-860°C. When heating, it needs to be preheated once or twice to ensure uniform heating.
The selection of the holding time should ensure the completion of the structural transformation and the degree of solid solution of the alloying elements. If the holding time is too short, the thermal hardness and tempering resistance of 1.2714 steel will be reduced.
- 1.2714 Steel Tempering
The tempering of 1.2714 steel should be carried out immediately after quenching.The tempering time should be sufficient, otherwise the hardness of the core of the material will be high, which will easily cause cracking
When cooling after tempering, attention should be paid to prevent the second type of temper brittleness,and at the same time perform secondary tempering. The tempering temperature is about 10°C lower than the first tempering temperature, and the holding time can be shortened by 20%-25%.
1.2714 Steel Hardness Vs Tempering temperature
Tempering Temperature,℃ | 400-480 | 500-550 | 570-650 |
Hardness,HRC | 42-46 | 38-41 | 32-36 |
1.2714 STEEL VS 1.2713 STEEL
Chemical Composition Comparison
Grade | C | Si | Mn | P | S | Cr | Ni | Mo | V |
1.2714/56NiCrMoV7 | 0.50-0.60 | 0.1-0.4 | 0.65-0.95 | ≤0.03 | ≤0.03 | 1.0-1.2 | 1.50-1.8 | 0.45-0.55 | 0.07-0.12 |
1.2713/55NiCrMoV6 | 0.50-0.60 | 0.1-0.4 | 0.65-0.95 | ≤0.03 | ≤0.03 | 0.6-0.8 | 1.50-1.8 | 0.25-0.35 | 0.07-0.12 |
From the above table,we can see the biggest difference lies in the content of Cr and Mo.Due to composition factors, the manufacturing cost of 1.2714 steel is slightly higher than that of 1.2713 steel, but the performance of the two is very close.1.2714 steel can be regarded as an upgraded version of 1.2713 steel.
Heat Treatment Data Comparison In Quenched and Tempered Condition
Grade | Quenching Temperature,°C | Quench Medium | Tempering Temperature,°C | Hardness after Tempering,HRC |
1.2714/56NiCrMoV7 | 830-870 860-900 | Oil Air | See Hardness-Tempering Temperature Curves as below | |
1.2713/55NiCrMoV6 | 830-870 | Oil | ||
Remarks | 1.2714/56NiCrMoV7:Oil Quenching at 850°C,Tempering at 500°C Minimum Hardness Requirement:44HRC | |||
1.2713/55NiCrMoV6:Oil Quenching at 850°C,Tempering at 500°C Minimum Hardness Requirement:40HRC |
Principal Applications Comparison
DIN 1.2713/55NiCrMov6 and DIN 1.2714/56NiCrMoV7 both belong to hot workng tool steel group,you can know from the grade name, they are very close in all aspects,but still a bit different, for example, in the application,they have different focuses.
1.2713 tool steel is mainy used for hammer forging dies for medium and small dimensions,while 1.2714 tool steel focus on hammer forging dies up to the largest dimensions,particularly also with heavy embossing; part dies, die holders, plungers for extrusion presses.
WHERE CAN YOU BUY HIGH-QUALITY 1.2714 STEEL?
When you do everything possible to buy high-quality 1.2714 steel but you are struggling to find a suitable manufacturer, we are here - PARMANU DHATU NIGAM !
We are a manufacturer of the highest quality special steel. We can fully meet your needs for 1.2714 steel, which stems from our rich manufacturing experience and strict quality control system.
What We Supply For DIN 1.2714/56NiCrMoV7 Steel
Supply Form | Size(mm) | Process | Tolerance | |
Round | Φ6-Φ100 | Cold Drawn | Bright/Black | Best H11 |
Φ16-Φ350 | Hot Rolled | Black | -0/+1mm | |
Peeled/ground | Best H11 | |||
Φ90-Φ1000 | Hot Forged | Black | -0/+5mm | |
Rough Turned | -0/+3mm | |||
Flat/Square/Block | Thickness :120-800 | Hot Forged | Black | -0/+8mm |
Width:120-1500 | Rough Machined | -0/+3mm |
Heat Treatment:Annealed(+A),Quenched & Tempered(+QT)
Machining:Turning/Milling/Drilling/Peeling/Polishing
DIN 1.2714 | JIS SKT4 | AISI L6 | UNI T61206 | ASTM L6 | Brand Name Sitherm 2714 | Ravne UTOPEX2 | Mat No 1.2714 | DIN 56NiCrMoV7+ | EN 55NiCrMoV7 | ГОСТ 5ХН2МФ | Hot Work Tool Steel | GB 5CrNiMo | AFNOR 55NCDV7 | BS BH224-5 | UNI 44NiCrMoV7-KU | UNI 56NiCrMoV7-KU | PN WNL | PN WNLV | CSN 19662 | CSN 19663 | ONORM W501 | ONORM W502 | GOST 5KHNM | GOST 5KHNV | ISO 55NiCrMoV7 | WNr 55NiCrMoV6 | WNr 56NiCrMoV7
1.2714 Hot work Tool Steel INDIA suppliers, wholesale, distributors and stockholder. PARMANU DHATU NIGAM is manufacturers and Have large quantity Stock in warehouse. We supply in Round bar, gauge plate steel, pipe / Tube,rod, square, hexagonal, blanks, plate, sheet, precision ground flat bar,
precision ground bar stock and hollow bar. provide black surface and black surface alloy steel material.
1.2714 is a German Hot work alloy steel material grade.it is shock
resisting steel. it belong to DIN 17350 standard. Digital Grade material
number W-Nr 1.2714, Metal Steel garde 56NiCrMoV7. It is a die steel,
use in extrusion moulds, Hot Cast moulds. like aluminium production,
Aluminium cast mold. Our Tool Steel material 100 % ultrasonic tested
with good price. Small size steel products make by hot rolled, large
size steel products make by forging.
1.2714 Steel material properties datenblatt as below:
Chemical composition data of Metal 1.2714 Hot work steel-DIN 17350-1980 (EN4957-2001)
C | Si | Mn | Ni | P | S | Cr | Mo | V |
0.5 – 0.6 | 0.1 – 0.4 | 0.6 – 0.9 | 1.5 – 1.8 | max 0.03 | max 0.03 | 0.8 – 1.2 | 0.35 – 0.55 | 0.05 – 0.15 |
Material equivalent of DIN 1.2714 steel
USA | Germany | China | Japan | France | England | Italy | Poland | Czechia | Austria | GOST | Inter |
– | DIN,WNr | GB | JIS | AFNOR | BS | UNI | PN | CSN | ONORM | GOST | ISO |
L6 | 55NiCrMoV6 | 5CrNiMo | SKT4 | 55NCDV7 | BH224-5 | 44NiCrMoV7-KU | WNL | 19662 | W501 | 5KHNM | 55NiCrMoV7 |
56NiCrMoV7 | 56NiCrMoV7-KU | WNLV | 19663 | W502 | 5KHNV |
Physical properties of 1.2714 Tool Steel
- Density: 7.85kg/m3
- Thermal conductivity:
- Forging ratio: 4:1 Minimum
- Microstructure:
- Magnetic:
Mechanical properties of Alloy Steel 1.2714
- Hardness: Annealling 255 HB max, Q+T: 58-38HRc, different hardness according different Tempering temperature.
- Yield strength:
Heat treatment of (55NiCrMoV7) 1.2714 hot work steel
- Annealing: Annealing temperature/℃: 680~710; After the annealing, degree of hardness ≤HBS: 250
- Quenching: Hardening temperature/℃: 840~870, Quenching in oil
- Tempering: Commonly used drawing temperature/℃: 400~650; tempering after-hardening values /MPa|400℃: 1770; tempering after-hardening values /MPa|500℃: 1570; tempering after-hardening values /MPa|600℃: 1320; tempering after-hardening values /MPa|650℃: 1180
- Normalizing:
Forged steel properties of hot work 1.2714 tool steel
For forging 1.2714 steel, Slowly Pre-heat, at Hot-working temperature/℃: 1050~850
Processing of Steel Material 1.2714 | 56NiCrMoV7
Otai Special provide the Grinding, milling , polishing, turning, drilling and others machining service as your required tolerances and size.
Packing of 1.2714 steel
By steel Wire Bundling then put in container, or as customer require packing.
DIN 1.2714 | JIS SKT4 | AISI L6 | UNI T61206 | ASTM L6 | Brand Name Sitherm 2714 | Ravne UTOPEX2 | Mat No 1.2714 | DIN 56NiCrMoV7+ | EN 55NiCrMoV7 | ГОСТ 5ХН2МФ | Hot Work Tool Steel | GB 5CrNiMo | AFNOR 55NCDV7 | BS BH224-5 | UNI 44NiCrMoV7-KU | UNI 56NiCrMoV7-KU | PN WNL | PN WNLV | CSN 19662 | CSN 19663 | ONORM W501 | ONORM W502 | GOST 5KHNM | GOST 5KHNV | ISO 55NiCrMoV7 | WNr 55NiCrMoV6 | WNr 56NiCrMoV7
1.2714 (56nicrmov7) / 55NiCrMoV7 Steel
55NiCrMoV7/1.2714 is an Ni alloyed die steel which has extreme toughness and good through hardening properties with very little size change after heat treatment.55NiCrMoV7/1.2714 is similar to AISI/SAE L6,and is used for making forging dies,hot shear knives,punches,backing plate,die holders,hot punching tools
Chemical Composition: 55NiCrMoV7 per EN ISO 4957; 1.2714 per DIN 17350 (Hot Work Tool Steel)
GRADE | NUMBER | C | Si | Mn | P | S | Cr | Mo | Ni | V |
55NiCrMoV7 | 0.50-0.60 | 0.10-0.40 | 0.60-0.90 | ≤ 0.030 | ≤ 0.030 | 0.80-1.20 | 0.35-0.55 | 1.50-1.80 | 0.05-0.15 | |
1.2714 | 0.50-0.60 | 0.10-0.40 | 0.65-0.95 | ≤ 0.030 | ≤ 0.030 | 1.00-1.20 | 0.45-0.55 | 1.50-1.80 | 0.07-0.12 |
55NiCrMoV7/1.2714 Hot Work Tool Steel Size & Tolerance & Process
Shape | Size(mm) | Process | Tolerance | Length(mm) |
Round | Φ6-Φ50 | Cold Drawn | H11 | 3000-5800 |
Round | Φ40-Φ120 | Hot Rolled | -0/+3mm | 3000-10000 |
Round | Φ120-Φ1000 | Hot Forged | -0/+3mm | 3000-10000 |
Flat/Square/Block | Thickness:120-800 Width:120-1500 |
Hot Forged | -0/+3mm | 500-6000 |
55NiCrMoV7/1.2714 Hot Work Tool Steel Heat Treatment
Annealing For 55NiCrMoV7/1.2714
1.Nominal Annealing temperature:650-700°C
2.Cool slowly in the furance
3.Maximum Brinell hardness of 255
Hardening and Tempering(QT) For 55NiCrMoV7/1.2714
1.Nominal Hardening temperature:830-870°C for oil,830-890°C for air.
2.Hold at the temperature then quench in oil or air.
3.Tempering as soon as possible when the temperature low to ambient temperature
4.Heat uniformly to the required temperature allowing a soaking time of two hours per 25mm of ruling section.
5.A second tempering is highly recommended.
6.keep the material out of the furnace ,then cool in the air
Tempering | ||||||
Temperature | 200 | 250 | 300 | 400 | 500 | 600 |
Hardness(HRC) | 55 | 54 | 53 | 49 | 45 | 39 |
Tensile strength | 1910 | 1850 | 1790 | 1630 | 1490 | 1210 |
Stress Relieving For 55NiCrMoV7/1.2714
1.Stress relieving should be carried out by heating to 650-700°C to reduce distortion during heat treatment.
2.Cooling in furnace to 300-350°C
3.Cooling in air
55NiCrMoV7/1.2714 Hot Work Tool Steel Mechanical Property( for reference only)
1.Tensile strength: 1220-1330MPa
2.Yield point: 1100MPa
3.Percentage reduction of area after fracture: 55%
4.Elongation after fracture: 14%
55NiCrMoV7/1.2714 Hot Work Tool Steel Delivery Condition
1.Shape:Round/Square / Flat/Shafts/Rollers/Blocks
2.Surface condition:Black surface/Bright surface
3.Heat Treatment:Annealed/QT
4.Straightness:Max 3mm/m(Enhanced straightness may be available on request)
5.Length:3000-5800mm suitable for 20″container. above 6000mm,suitable for 40″ container
6.Grain Size: 5-8 acc to ASTM E112-96
7.Typcial Hardness:HRC60-65
8.Ultrasonic Standard: Sep1921/ASTM A388/EN 10228-3
9.Non Metallic Inclusion: 2 max acc to ASTM E45 /K4≤20 acc to DIN 50602
10.Forging Ratio: minimum 4 : 1
11.Marking: Grade/Weight/Length/Size/Heat Number
55NiCrMoV7/1.2714 Hot Work Tool Steel Quality Certification
A material test report(Inspection Certificate EN 10204 3.1) will be provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non Metallic Inclusion
5.Heat Treatment Process
6.Grain size
7.Forging ratio
8.NDE test method/criteria
55NiCrMoV7/1.2714 hot work tool steel manufacturers and suppliers, supplied in round rods,square/flat bars,rollers,shafts,blocks and forging pieces.
Other Related Hot Work Tool Steel
AISI H11 Tool Steel
1.2343 / X37CrMoV5-1 Tool Steel
1.2714 (56nicrmov7) / 55NiCrMoV7 Steel
L6 Steel | AISI L6 | 1.2714 | SKT4
H13 Steel | AISI H13 | 1.2344 | SKD61
H11 Steel | AISI H11 | 1.2343 | SKD6
1.2714 Steel – The Ultimate FAQ Guide
Are you looking to uncover the truth behind what 1.2714 steel is? Do you want to learn more about this particular kind of steel to properly figure more out about it?
In this guide, we’ll help you have a better and a deeper understanding of what the 1.2714 steel is. We will help you see it at a better angle to the extent that you’ll know every inch and bit of it!
What is DIN 1.2714 Steel?
It’s a type of steel that you can use for hot working tool sets, specifically in the plastic mold industry.
Image of how the DIN 1.2714 steel looks like
Thanks to its large amounts of Chromium and Nickel, you can expect it to have high levels of toughness and hardening properties.
You can find DIN 1.2714 as a 40 HRC standard grade that possesses uniform hardness plus good hardenability.
DIN 1.2714 Equivalent Steel
DIN is a European standard and is the abbreviation of Deutsches Institut für Normung, in English, it is the German Institute of Standardization.
Since the DIN 1.2714 is under this particular standard, there are other standards that have this particular steel. While they’re similar in terms of what elements are present, they’re different in terms of the content levels.
The equivalent steels for DIN 1.2714 are:
- AFNOR 55 NCD V7
- Euronorm 55 NiCrMo V7
- DB6
- AISI L6 Steel
What are the Characteristics of 1.2714 Steel?
Annealed state is extremely workable and efficient
Some of the most notable traits and specific characteristics of DIN 1.2714 steel include:
- High hardness levels after hardening process
- Good levels of tempering resistance
- Resistant in sudden temperature changes
- Thermal fatigue adaptability
- Can be hardened in both oil (830 to 870 degrees Celsius) and air (870 to 900 degrees Celsius)
- Workable even while its softly annealed
What is the 55NiCrMoV7 Steel?
This particular steel grade is similar to the DIN 1.2714, it’s just the new term for it because it follows the Euronorm format, not the DIN.
Quick sample of the 55NiCrMoV7 steel
The Euronorm standard is a standard that replaced the DIN, along with some other standards in the industry, such as BS, NF, and SS.
DIN 1.2714 Mechanical Properties
The mechanical properties of DIN 1.2714 steel are important because these are what you’ll be using them for.
You ought to know these information for you to distinguish whether or not you’ll be able to use them for the application you want. The mechanical properties of DIN 1.2714 steel includes:
- (HB) Hardness: 376
- Rm Tensile Strength:MPa 1270; ksi 184
- Rp 0.2 Yield Strength: MPa 1045; ksi 151
- Elongation: 10%
- Elastic Modulus:GPa 205; ksi 29733
For Which Applications Can You Use DIN 1.2714 Steel?
You can find use of the DIN 1.2714 steel in a wide array of sectors and industries.
Forming dies – one of the most customary applications you can have for 1.2714 steel
The most common applications you can have for this particular steel grade include:
- Clutch Parts & Pins
- Punches
- Forming Rolls
- Spindles
- Bearings
- Chuck Parts
- Knuckle Pins
- Pawls
- Trimmer Dies
- Blanking and Forming Dies
- Hot Punching Tools and Shear Knives
These aren’t the only applications you can have with DIN 1.2714 steel; there are a lot more!
What’s the Dimensional Program You Can Get 1.2714 Steel For?
The usual thickness that you can purchase it for is between the range of 8 and 120 mm. For the width, it’s in the range of 1,000 to 2,100 mm.
NOTE: You can get custom DIN 1.2714 steel if you want thicknesses and width that’s higher or above the usual. You just need to tell your manufacturer about it.
DIN 1.2714 Steel Chemical Composition
For you to have a better understanding of what 1.2714 steel is, here is its chemical composition:
Nickel (Ni) | Chromium (Cr) | Molybdenum (Mo) | Silicon (Si) | Phosphorus (P) | Sulfur (S) | Manganese (Mn) | Carbon (C) |
1.50 to 1.80% | 1.00 to 1.20% | 0.45 to 0.55% | 0.10 to 0.40% | ≤ 0.030% | ≤0.030% | 0.65 to 0.95% | 0.50 to 0.60% |
How is DIN 1.2714 Made and Manufactured?
Generally, alloyed steel is made through the mixture or the combination of plain carbon steel with alloying elements.
The creation and the manufacturing of DIN 1.2714 steel is like this, and employs the melting of carbon steel along with other alloying elements to form a better and a more specific material.
You can manufacture DIN 1.2714 through the melting all of the alloying elements mentioned above in either a casting operation or a furnace. It’s done in a closed and a controlled area to refrain from oxidation and contamination of the steel.
Can You use 1.2714 Steel in Hot Work Applications?
You can use DIN 1.2714 in hot work applications successfully
Yes, as a matter of fact, DIN 1.2714 steel is specifically made for use in hot working applications because of the toughness and the ductility that it offers.
Where Can You Purchase High Quality 1.2714 Steel?
Wherever you look and whatever type of manufacturing company you work with, you’ll never be able to find a DIN 1.2714 steel manufacturer as adept and as skilled as us at PARMANU DHATU NIGAM.
We’re the best and the most experienced alloyed steel manufacturer and you can count and bank on us to help you in producing 1.2714 steels.
Whether you need round steel bars, flat steel bars, or plates, we got you! DIN 1.2714 is just one of the many alloyed steels we have in our arsenal, we offer a lot more!
Don’t hesitate to give us a call here at PARMANU DHATU NIGAM if you need further help with 1.2714 steel! We can specify and customize your orders based on size, dimensions, supply forms and shapes – and even composition
Contact us today by shooting us a email or by dialing our hotline! We will grant you a free quotation or a free estimate to help you out with budgeting!
Does PARMANU DHATU NIGAM Offer a Free Sample?
So long as you know what you want specifically, we can help you out by giving you a free sample product, too!
Work with PARMANU DHATU NIGAM and get world-class quality DIN 1.2714 steel in the best rates and prices!
DIN 1.2714 | JIS SKT4 | AISI L6 | UNI T61206 | ASTM L6 | Brand Name Sitherm 2714 | Ravne UTOPEX2 | Mat No 1.2714 | DIN 56NiCrMoV7+ | EN 55NiCrMoV7 | ГОСТ 5ХН2МФ | Hot Work Tool Steel | GB 5CrNiMo | AFNOR 55NCDV7 | BS BH224-5 | UNI 44NiCrMoV7-KU | UNI 56NiCrMoV7-KU | PN WNL | PN WNLV | CSN 19662 | CSN 19663 | ONORM W501 | ONORM W502 | GOST 5KHNM | GOST 5KHNV | ISO 55NiCrMoV7 | WNr 55NiCrMoV6 | WNr 56NiCrMoV7
Andaman and Nicobar Islands Andhra Pradesh Arunachal Pradesh Assam Bihar Chandigarh Chattisgarh Chhattisgarh Dadra and Nagar Haveli Daman and Diu Delhi Goa Gujarat Haryana Himachal Pradesh Jammu and Kashmir Jharkhand Jamshedpur Karnataka Kerala Lakshadweep Madhya Pradesh Maharashtra Manipur Meghalaya Mizoram Nagaland Orissa Odisha Puducherry Punjab Rajasthan Sikkim Tamil Nadu Telangana Tripura Uttarakhand Uttaranchal Uttar Pradesh West Bengal
Adilabad Agartala Agra Ahmedabad Ahmednagar Ajmer Akola Alappuzha Aligarh Allahabad Alleppey Alok City Aluva Alwar Alwaye Amalapuram Ambala Ambarnath Ambattur Ambernath Ambur Amravati Amritsar Anand Anantapur Anantapuramu Angul Anjar Ankleshwar Anklesvar Asansol Aurangabad Avadi Baddi Bagalkot Bahadurgarh Baharampur Ballari Ballarpur Bangalore Bardhaman Bardoli Bareilly Barrackpore Bathinda Becharaji Belagavi Belgaum Bellary Bengaluru Berhampore Berhampur Bhadravathi Bhadravati Bhadreswar Bhagalpur Bharatpur Bharuch Bhatapara Bhatpara Bhavnagar Bhilai Bhilwara Bhimavaram Bhiwadi Bhiwandi Bhiwani Bhopal Bhubaneswar Bhuj Bidar Bijapur Bikaner Birlanagar Bokaro Bokaro Steel City Bongaigaon Brahmapur Broach Budge Budge Bulandshahr Burnpur Calcutta Calicut Chaibasa Champdani Chandigarh Chandrapur Channapatna Charkhi Dadri Chennai Cherthala Chikkamagaluru Chinchwad Chittaranjan Chittoor Cochin Coimbatore Cuddalore Cuttack Dalkhola Dalmianagar Damanjodi Dandeli Dankuni Darbhanga Darjeeling Davanagere Davangere Dehradun Delhi Dewas Dhanbad Dhanbad City Dharmapuri Dharwad Dhule Dibrugarh Digboi Dindigul Dum Dum City Durgapur Eluru Ennore Ernakulam Erode Faridabad Firozabad Gadchandur Gajraula Gandhidham Gandhinagar Gaya Ghaziabad Goa Gorakhpur Gulbarga Guntur Gurgaon Gurugram Guwahati Gwalior Habra Haldia Haldwani Halisahar Haora Haridwar Hassan Hazaribagh Hisar Hooghly Hosapete Hosdurg Hoshiarpur Hospet Hosur Howrah Hubballi Hubli Hugli Hyderabad Ichalkaranji Idukki Township Indore Induru City Jabalpur Jagatdal Jaipur Jajpur Jalandhar Jalgaon Jammu Jamnagar Jamshedpur Jangipur Jetpur Jhansi Jharia Jharsuguda Jind Jodhpur Jorhat Junagadh Kadapa Kagithapuram Kaithal Kakinada Kalaburagi Kalburgi Kalimpong Kalinga Kalinga Nagar Kalpakkam Kalyan Kalyani Kamarhati Kanchrapara Kannur Kanpur Karimnagar Karnal Karur Kashipur Katwa Khammam Khammamett Khandwa Kharagpur Khardaha Khargaon Kheda Kochi Kodagu Kolar Kolhapur Kolkata Kollam Kollegal Kollegala Koodankulam Koraput Korba Kota Kottayam Kozhikode Kudankulam Kunnamkulam Kurnool Kurukshetra Latur Lucknow Ludhiana Madanapalle Madurai Mahesana Malappuram Malda Malegaon Mandya Mangalore Mangaluru Manjeri Manmad Margao Mathura Medinipur Meerut Mehsana Mirzapur City Modinagar Mohali Moradabad Morbi Morvi Mumbai Muvattupuzha Muzaffarnagar Muzaffarpur Mysore Mysuru Nadiad Nagaon Nagda Nagercoil Nagpur Naihati Nalgonda Nandambakkam Nanded Waghala Nandyal Nandyala Nangal Narnaul Nashik Navi Mumbai Navsari Neemuch Nellai Nellore Nepanagar New Delhi Neyveli Nimach Nizamabad Noida Noonmati Ongole Ooty Padajhar Khurd Palakkad Palghar Palghat Pali Palwal Panchkula Panihati Panipat Panjim Panna Paradeep Patiala Patna Perambra Perambur Pimpri Pimpri-Chinchwad Pinjore Pithampur Prayagraj Punalur Pune Raebareli Raichur Raiganj Raigarh Raipur Rajahmundry Rajkot Rampurhat Ranchi Rayagada Renukoot Rewa Rewari Rishikesh Rishra Rohtak Roorkee Rourkela Rudrapur Rupnarayanpur Saharanpur Salem Sambalpur Sangli Satara Secunderabad Seoni Shahdara Shamnagar Shantiniketan Shibpur Shimoga Shivamogga Sikar Silchar Siliguri Silvassa Sindri Singhbhum Sirpur Sirsa Sivakasi Sodepur Solapur Sonipat Sreerampur Sri City Sri Ganganagar Sriharikota Srikakulam Srinagar Sriperumbudur Surat Surendranagar Suri Tambaram Tanuku Tarapur Thane Thanjavur Thiruvananthapuram Thiruverumbur Thodupuzha Thoothukudi Thrissur Tinsukia Tiruchirappalli Tirunelveli Tirupati Tiruppur Tiruvalla Titagarh Tribeni Trichy Trivandrum Trombay Tumakuru Tumkur Tuticorin Udaipur Udhana Udupi Ujjain Unnao Vadodara Valsad Vandalur Vapi Varanasi Vellore Veraval Vijayanagara Vijayapura Vijayawada Villupuram Viluppuram Visakhapatnam Vizhuppuram Vizianagaram Warangal Warora Wayanad Yamunanagar Zaina Kot
Afghanistan Albania Algeria Andorra Angola Antigua and Barbuda Argentina Armenia Australia Austria Azerbaijan Bahamas Bahrain Bangladesh Barbados Belarus Belgium Belize Benin Bhutan Bolivia Bosnia and Herzegovina Botswana Brazil Brunei Bulgaria Burkina Faso Burundi Cambodia Cameroon Canada Cape Verde Central African Chad Chile China Colombia Comoros Congo Costa Rica Cote D'Ivoire Croatia Cuba Cyprus Czechia-Czech Republic Denmark Djibouti Dominican Republic Ecuador Egypt El Salvador England Equatorial Guinea Eritrea Estonia Eswatini-Swaziland Ethiopia Europe Fiji Finland France Gabon Gambia Georgia Germany Ghana Greece Grenada Guatemala Guinea-Bissau Guyana Haiti Holy See Honduras Hong Kong Hungary Iceland India Indonesia Iran Iraq Ireland Israel Italy Jamaica Japan Jordan Kazakhstan Kenya Kiribati Kosovo Kuwait Kyrgyzstan Laos Latvia Lebanon Lesotho Liberia Libya Liechtenstein Lithuania Luxembourg Macau Madagascar Malawi Malaysia Maldives Mali Malta Marshall Islands Mauritania Mauritius Mexico Micronesia Moldova Monaco Mongolia Montenegro Morocco Mozambique Myanmar-Burma Namibia Nauru Nepal Netherlands New Zealand Nicaragua Niger Nigeria North Korea North Macedonia Norway Oman Pakistan Palau Palestine Panama Papua New Guinea Paraguay Peru Philippines Poland Portugal Puerto Rico Qatar Romania Russia Rwanda Saint Kitts and Nevis Saint Lucia Saint Vincent and the Grenadines Samoa San Marino Sao Tome and Principe Saudi Arabia Senegal Serbia Seychelles Sierra Leone Singapore Slovakia Slovenia Solomon Islands Somalia South Africa South Korea South Sudan Spain Sri Lanka Sudan Suriname Sweden Switzerland Syria Taiwan Tajikistan Tanzania Thailand Timor-Leste Togo Tonga Trinidad and Tobago Tunisia Turkey Turkmenistan Tuvalu Uganda Ukraine United Arab Emirates UAE United Kingdom United States US Uruguay Uzbekistan Vanuatu Vatican City Venezuela Vietnam Yemen Zambia Zimbabwe
MIDDLE EAST : Saudi Arabia Iran Ira Qatar Bahrain Oman Kuwait Turkey Yemen Syria Jordan Cyprus
ASIA : Singapore Malaysia Indonesia Thailand Vietnam South Korea Japan Sri Lanka Maldives Bangladesh Myanmar Taiwan Cambodia
EUROPE : Russia Norway Germany France Italy UK Spain Ukraine Netherlands Belgium Greece Czech Republic Portugal Hungary Albania Austria Switzerland Slovakia Finland Ireland Croatia Slovenia Malta
AFRICA : Nigeria Algeria Angola South Africa Libya Egypt Sudan Equatorial Guinea the Republic Of Congo Gabon
SOUTH AMERICA : Argentina Bolivia Brazil Chile Venezuela Colombia Ecuador Guyana Paraguay Uruguay
NORTH AMERICA : US Canada Mexico Panama Costa Rica Puerto Rica Trinidad And Tobago Jamaica Bahamas Denmark
Allen Cap Head Bolt Bar Blind Flange Bolt Bushing Butt Weld Fitting Butt Weld Outlet Circle Coil Countersunk Bolt Countersunk Screw Coupling Cross Elbow End Cap Fabrication Fastener Fitting Flange Flat Bar Foil Hex Head Bolt Hex Head Screw Hexagon Bar Hexagon Head Bolt Hexagon Head Male Hexagon Socket Head Cap Screw Hexagonal Bar Hollow Bar Lap Joint Flange Nipple Nut Perforated Sheet Pipe Pipe Fitting Plate Powder Rectangular Bar Reducer Ring Rod Round Bar Sheet Shim Slip On Flange Socket Cap Head Screw Socket Head Cap Screw Socket Weld Fitting Socket Weld Flange Socket Weld Outlet Socket Welding Flange Square Bar Strip Stud Bolt Stud End Tee Threaded Fitting Threaded Flange Threaded Outlet Threaded Rod Tube Tubing Union V Band Flange Valve Washer Welding Electrodes Welding Neck Flange Wire Wire Mesh
DIN 1.2714 | JIS SKT4 | AISI L6 | UNI T61206 | ASTM L6 | Brand Name Sitherm 2714 | Ravne UTOPEX2 | Mat No 1.2714 | DIN 56NiCrMoV7+ | EN 55NiCrMoV7 | ГОСТ 5ХН2МФ | Hot Work Tool Steel | GB 5CrNiMo | AFNOR 55NCDV7 | BS BH224-5 | UNI 44NiCrMoV7-KU | UNI 56NiCrMoV7-KU | PN WNL | PN WNLV | CSN 19662 | CSN 19663 | ONORM W501 | ONORM W502 | GOST 5KHNM | GOST 5KHNV | ISO 55NiCrMoV7 | WNr 55NiCrMoV6 | WNr 56NiCrMoV7
Dealers | Distributors | Exporters | Importers | Manufacturers | Suppliers | Stockists | Wholesalers
DIN 1.2714 Round Bar | JIS SKT4 Round Bar | AISI L6 Round Bar | UNI T61206 Round Bar | ASTM L6 Round Bar | Brand Name Sitherm 2714 Round Bar | Ravne UTOPEX2 Round Bar | Mat No 1.2714 Round Bar | DIN 56NiCrMoV7+ Round Bar | EN 55NiCrMoV7 Round Bar | ГОСТ 5ХН2МФ Round Bar | Hot Work Tool Steel Round Bar | GB 5CrNiMo Round Bar | AFNOR 55NCDV7 Round Bar | BS BH224-5 Round Bar | UNI 44NiCrMoV7-KU Round Bar | UNI 56NiCrMoV7-KU Round Bar | PN WNL Round Bar | PN WNLV Round Bar | CSN 19662 Round Bar | CSN 19663 Round Bar | ONORM W501 Round Bar | ONORM W502 Round Bar | GOST 5KHNM Round Bar | GOST 5KHNV Round Bar | ISO 55NiCrMoV7 Round Bar | WNr 55NiCrMoV6 Round Bar | WNr 56NiCrMoV7 Round Bar