Description

Leaded Beryllium Copper UNS C17300 Plate is a heat treatable, ductile, and mill hardened alloy with a tensile strength of 1380 MPa (200 ksi). It has a lead content ranging from 0.2 to 0.6%. The addition of lead reduces chipped-edges during the use of cutting tools, which decreases tool wear. Leaded Beryllium Copper UNS C17300 is a beryllium copper alloy. It has the following properties: Tensile strength: 1380 MPa (200 ksi) Density: 8.25 g/cm3 Elastic modulus: 13.40 kg/mm2 Thermal expansion coefficient: 17 x 10-6 Melting point: 870°C -980°C Corrosion resistance: Good to excellent Cold workability: Excellent Hot formability: Good Tensile strength: 275 - 345 MPa Yield: 15.0 - 30.0% Elongation at break: 125 - 130 GPa Modulus of elasticity: 0.300 UNS C17300 beryllium copper alloys are heat treatable, ductile, and can be mill hardened. They are suitable for applications requiring good conductivity, high strength, and stiffness. C17300 is suitable for applications requiring good conductivity, high strength, and stiffness. Typical uses include: Electrical: Contact bridges, electrical switch and relay blades, electric motor components, navigational instruments, clips, electrical connectors, connectors, relay parts, switch parts, fuse clips Fasteners: Washers, screws, bolts, retaining rings, roll pins, lock washers, fasteners Here are some places that sell Leaded Beryllium Copper UNS C17300 Plate: